| Material | Feed size | Final fineness | |
|---|
| 2x seeds (rape and flex) | 2-4mm | < 0,5mm | details |
| Acrylate plastic | < 6 cm | < 0,25 mm | details |
| Acrylic textil fibres | < 3mm | < 200µm | details |
| Activated carbon | 5 mm | < 100 µm | details |
| Activated carbon (ball-shaped) | < 2mm | < 0,2mm | details |
| Activated carbon (coarse = 1, fine=2) | < 3mm | 99,3% < 45µm | details |
| Activated coal | < 100µm | as fine as possible | details |
| Agar-agar | 10x15mm | d90 < 30µm | details |
| Al-Va-alloy (1-2); corundum-slag (3-4); Mo-Al-alloy (5-7) | < 15cm | < 160µm | details |
| Al2O3 (Tabularna Glinica) | < 10 mm | d50 < 5 µm | details |
| Alexandrite (synthetic) | <8mm | < ap 200µm | details |
| Algea (dry) | < 2 cm | < 2 mm | details |
| Alginate (freeze dried, extra pure) | < 3mm | < 20µm | details |
| Alpha-tricalcium phosphate | < 15mm | < 500µm | details |
| aluminate | 30 mm | < 8 mm | details |
| aluminium nitride | 30x30mm | <100µm | details |
| Aluminium oxide | < 70µm | d50 < 50nm | details |
| Aluminium oxide | <150µm | d50 < 350nm | details |
| Aluminium oxide | < 0,5-1mm | d90 < 5µm | details |
| Aluminium oxide (tablets) | 11x9mmØ | <300-350µm | details |
| Aluminum - foil | 5 mm | < 250 µm | details |
| Amaranths and Flax Seeds | < 2 mm and < 4 mm | < 1 mm | details |
| Amber | ~ 5mm | < 0,2mm | details |
| Ammonium Sulphate | 2 mm | < 0,12 mm | details |
| Amorphous silicic acid | < 250 µm | 83.3% < 10µm | details |
| Amorphous silicic acid | < 250 µm | d90 < 10µm | details |
| Anhydrit | 40.0 mm | 50 % < 100.0 µm | details |
| Animal Feed Flour | < 3 mm (mainly) | < 0,5 mm | details |
| animal food | 1-2mm | <250µm | details |
| Antimony (trial 1), Tellurium (trail 2) | < 200µm | d50 < 250nm | details |
| antracite coal | 3 mm | 315-400 µm | details |
| Apple (brittle, dried) | ~ 3 cm | < 0,5 mm | details |
| Artificial Sweetener Tablets | ~ 4 mm | d50 < 100 µm | details |
| asbestos | 250 µm (long fibers) | d50 < 100 nm (d50 < 122 nm reached) | details |
| Ashes (with wooden pieces and metal fragments) | 2cm | app. 200µm | details |
| Asparagus (fresh) | 50 mm | 100 % < 2 mm | details |
| asphalt-plate | < 6 cm | < 2 mm | details |
| Baked Goods | < 10 cm | < 1 mm | details |
| Barium nitrate | < 10-15 mm | < 100 µm | details |
| Barium titanate | < 80 µm | d50 < 10 nm | details |
| barley | 1cm | < 500µm | details |
| Barley (barleycorn) | < 1 cm | < 1 mm | details |
| basalt | 8 mm | d90 < 71µm | details |
| batteries (dry) | < 4 cm | < 2 cm | details |
| beans | 6mm Ø | <500µm | details |
| Bee propolis | 10 mm | 100 % < 300 µm | details |
| Bentonite | < 3 cm | < 2 mm | details |
| Bentonite | <25µm | d50< 600nm | details |
| Bentonite (dry) | 1cm | 16.7% > 63µm | details |
| BENTONITE CLAY | < 100 µm | d50 < 100 nm (d50 < 120 nm reached) | details |
| biochar | < 2 cm | d50 < 20 µm | details |
| Biopolymer (chitosan) | < 2cm | < 80µm | details |
| Birds Eye Chilies | 30.0 mm | < 500 µm | details |
| Bitumen | < 6cm | < 1cm | details |
| Bois (wood) | 5 mm | < 80µm | details |
| bones | 2–3 cm | app. 400µm | details |
| bones (dried - beef) | < 3 cm | < 10 mm | details |
| Bones (dry without marrow) | 25.0 mm | 100.0 % < 750.0 µm | details |
| Brake lining | < 15 mm | d50 < 41 µm | details |
| brick | 8 mm | < 63 µm | details |
| burned lime | 3 cm | 90 µm (up to 90 % < 90 µm can be reached) | details |
| Ca-pantothenate | < 300µm | d50 < 10µm | details |
| Cadmium (Cd) | 1.6 mm | 40.0 % < 0.6 mm | details |
| Calcium Carbonate | 200.0 µm | d50 < 1 µm | details |
| Calcium Carbonate | < 800 µm | d50 < 10 µm | details |
| calcium turnings ; magnesium turnings | 2,5cm | --- | details |
| Calciumcarbonate (result 1), Magnesiumhydroxidcarbonat (result 2-3) | 20 µm | 100% < 7µm*2 | details |
| candy (soft gum) | 25 mm | < 100 µm | details |
| Caoline mixture K2 (see No1); K4 (see No2&3) | d50 <20µm | d50<0,3µm | details |
| Carbon Black | 6 mm | < 80 µm | details |
| Carrageenan | 250µm | 98,7% < 71µm | details |
| Cassia Legnea | 15mm*1 | <0,5mm | details |
| cast iron | 15 mm (max. 6 mm thick) | < 200 µm | details |
| Cast Iron samples | 35 mm | < 4 mm (thickness) | details |
| Catalyst | 12 cm | < 500 µm | details |
| Catalyst Recycling Material | < 6 cm | d50 < 16µm | details |
| CBD-Cannabis buds (dried) | < 30 mm | 90 % < 2 mm | details |
| CCA pine wood cubes | 6x6x6mm | < 300µm | details |
| Cellulose | mm | 90.0 % < 0.5 mm | details |
| Cellulose | ~ 70 cm long | < 0,1 mm | details |
| Cellulose | < 3 cm | < 1 mm | details |
| Cellulose diacetate | 15 x 3 mm | < 500 µm | details |
| cement | < 3 mm | d90 < 60 µm | details |
| cement (2 samples) | < 15 mm | < 1 mm | details |
| Cement (high aluminia) | < 10mm | < 150µm | details |
| Cement clinker | < 3mm | d50 < 50µm (d50 <12,6µm reached) | details |
| Cement panel | < 18 cm | < 10 µm | details |
| Cement paste (dried at 105 °C) | 20 mm | 90.0 % < 125.0 µm | details |
| ceramic | 2 cm | 90 % < 1mm | details |
| Ceramic catalyst | app. 5 cm | < 50 µm | details |
| Cereals, Lot 6.3 | < 6 mm | < 0,2 mm | details |
| Cerium oxide | 1.0 µm | 0.25 % < 0.375 µm | details |
| Cerium oxide/copper oxide (90%/10%) | < 30µm | mechanochemical reaction | details |
| Chalk | < 10mm | d90 < 20µm | details |
| charcoal | < 1 cm | < 200 µm | details |
| Charcoal Powder | < 0,2mm | d50 < 3µm | details |
| Chewing gum (without glaze) | 22 mm | < 500 µm | details |
| china clay (moistened) | 3 cm | < 8 mm | details |
| Chocolate | < 1 cm | < 1,5 mm | details |
| Clay | 5.0 cm | 1.0 % < 1.0 mm | details |
| Clay | < 6 cm | d50 < 63 µm | details |
| Clay and Soil | < 30 mm | < 2 mm | details |
| clinker | < 1 cm | < 180 µm | details |
| clinker | < 20 mm | < 200 µm | details |
| clinker | 50 x 30 mm | 0,1 mm | details |
| Clinker | 8 mm | < 100µm | details |
| clinker | < 60mm | < 0,5 mm | details |
| Cloth (cotton, green-checkered) | app. 5x4cm | < 1 mm | details |
| Coal | < 2cm | 94% < 20µm | details |
| Coal | < 500µm | d50 < 650nm | details |
| Coal | 20 mm | d90 < 250 µm | details |
| coal | < 10mm | d90 < 250µm | details |
| coal | < 15 mm | 160-250 µm | details |
| Coal seam material | < 30 mm | d50 < 5µm | details |
| coating powder | 2 cm | 50 % < 35.85 µm | details |
| cocoa -pellets | ~ 1 cm | d90 < 150 µm | details |
| Cocoa beans | 5mm | < 100µm | details |
| Cocoa Nibs | 15.0 mm | 50 % < 300 µm | details |
| coconut fibres | < 2 cm (long) | < 100 µm | details |
| Coffee beans (roasted) | 10 mm | 100 % < 2 mm | details |
| coffee beans (roasted) | < 10mm | < 0,5mm | details |
| coke | < 35 mm (long) | < 0,5 mm | details |
| coke | 4 mm | < 0.8 mm | details |
| coke | < 15mm | < 100µm | details |
| Cokes & SiO2 | < 5 mm | < 2 mm | details |
| collagen/axismaterial | 15 mm | < 500µm | details |
| Colophony (+ Magnesium oxide) | 10 mm | < 100 µm | details |
| Compost (dried) | 60-80 mm | < 0,5 mm | details |
| compost (wet) | < 4 mm | < 100µm | details |
| Computer mainboard | < 2cm | ~250 µm | details |
| conches | 30-40 mm | 100-300 µm | details |
| concrete | 6 cm | < 8 mm | details |
| concrete | 6 cm | < 8 mm | details |
| concrete drilling cores | 5 mm | < 300 µm | details |
| copper ore | 150 µm | < 50µm (57 % < 50 µm reachable) | details |
| copper oxichloride (untreated, raw salt) | < 20µm | < 1.5µm | details |
| Cordierite glass (3 samples) | < 0,7 mm | < 15 µm | details |
| Cork | 5x2 cm | < 0,25 mm | details |
| corn | < 8 mm | < 0,5 mm | details |
| Corn | grains | homogenous powder | details |
| corn straw | < 4mm | < 300µm | details |
| cotton wool | 7 cm | < 400 µm | details |
| Cow parts (ear ;ox tail; minced meat) | 5.0 cm | 100.0 % < 1 mm | details |
| Cricket (dry) | 3.0 cm | 50 % < 0.1 mm | details |
| Ctitrus Fibers | 3.0 mm | 50.0 % < 50.0 µm | details |
| Cucumber | 30 cm | 95 % < 1 mm | details |
| Cuprous Chloride | 100µm | d50 5,5µm | details |
| curd soap | < 2 cm | < 800 µm | details |
| DATE SEED POWDER | < 3mm | d50 <7µm (d50 < 11µm reached) | details |
Dental composite filler coarse (trials 1-2)
and fine quality (trials 3-4) | 5mm | d50 <1,7µm | details |
| Diamond/silicon carbide (95%/3%) | 5mm | < 1mm | details |
| Diatomite | ~ 150 µm | d50 < 5 µm | details |
| Dog Food | 10.0 mm | 50.0 % < 1.0 mm | details |
| draff | | | details |
| Dried biomass | 12 mm | < 250 µm | details |
| Dried Carrot Residues | 0 | 50.0 % < 250.0 µm | details |
| dried plants | <20-30mm | homogenous powder | details |
| Drilling core (concrete) | 6 cm | < 10 mm | details |
| drilling core (disk) | 50 mm Ø | < 500 µm | details |
| dry waste material | 8-10 cm | < 0,25 mm | details |
| E-fibre optics | 4mm | 80µm | details |
| EDTA (Ethylenedinitrilotetraacetic acid) | app. 300 µm | d90 < 25µm | details |
| Elastomer (NBR) | ca. 5mm | <200µm | details |
| Elder | 10 cm | < 2 mm | details |
| electronic junk (P1 und P2) | 10 mm | < 500µm | details |
| electronic waste | < 1 cm | < 500 µm (or finer) | details |
| Electronics Components | 1.0 cm | 90 % < 1.0 mm | details |
| Endosperm | 4mm | < 80µm | details |
| Epoxy polyester | < 2cm | <0,12mm | details |
| EVA - discs/ foil | < 5 cm | < 4 mm | details |
| Extruded PVC | 150 mm | 99,5 % < 4.0 mm | details |
| feldspar | < 7mm | d50 < 15µm | details |
| fennel | grains | < 0,2mm | details |
| Ferro chrome | < 5 cm | < 1 cm | details |
| Ferro tungsten | 2 cm | < 120µm | details |
| Ferro tungsten (75%) | < 2,5cm | < 200 µm | details |
| Ferro vanadium | < 1 cm | < 500µm (< 150µm reached) | details |
| Ferrochrome | < 8mm | 67%< 200µm 93% < 200µm | details |
| Ferrochrome | 3-4mm | <160µm | details |
| Ferromolybdenum | < 5cm | < 63µm | details |
| Ferromolybdenum alloy | 6 cm | < 100 µm | details |
| Ferrotitanium | < 6cm | < 100µm | details |
| Ferrotitanium | < 3,5 cm | < 0,1-0,5 mm | details |
| fertilizer | 5 – 6mm | app. 70% < 60µm | details |
| fibres of bamboo | < 50 mm | < 1 mm | details |
| field bean (Vicia faba) | < 20mm | < 0,5 mm | details |
| Filber-Samples (Hops and other) | 3.0 cm | 95 % < 100.0 µm | details |
| Fish (fresh, trout) | 25 cm | < 6 mm | details |
| Fish bones (dry) | 2-3cm | < 0,25mm | details |
| fish flour (dark, agglomerated) | < 2 cm | < 1 mm | details |
| fluorspar | 250µm | < 25µm (96% reached) | details |
| Flux Fusion | 30.0 mm | 50.0<500.0 µm | details |
| Fly Ash | 75.0 µm | d50 < 1000 nm | details |
| Fly Ash (dry - mostly SiO2) | 100 µm | < 200 nm (d90 < 250 nm reached) | details |
| Formsand (feucht) | | | details |
| Four kinds of glass | 3,5-6cm | < 100µm | details |
| Gamma Aluminium Oxid | 25µm | 5µm | details |
| garnet | < 500 µm | 90% < 70µm | details |
| gelatine | 2 - 3cm | < 4mm | details |
| Glass | d95 < 20 µm | d50 < 8 µm | details |
| Glass | 45x20mm | < 30µm | details |
| glass | < 1cm | < 50µm | details |
| glass | < 5 cm | < 5 mm | details |
| glass | 10 mm | 75% < 100µm | details |
| glass | 2-3 cm | < 500 µm | details |
| glass | < 20mm | d90 < 5µm | details |
| glass | <3-4mm | 82,3%<5µm | details |
| glass (2 samples; short & long; both are moistened) | < 30 cm | d50 < 1µm | details |
| Glass (white) | < 4 cm | < 5 mm | details |
| Glass drops | < 3x0,5 cm | < 25 µm | details |
| Glass Frit | 120µm | 100% < 4µm | details |
| glass frit | < 20 mm | ca. 100µm | details |
| Gloriosa Superba fruits (dry) | < 5 mm | < 1 mm | details |
| gold dust | <120µm | flocculating | details |
| gold leaf | ~ 5mm | ~ d90<10µm | details |
| Granite | < 15 mm (long) | 400-800 µm | details |
| granite | < 2cm | < 63µm | details |
| Granite | 3 mm | < 71 µm | details |
| Graphite | 15.0 mm | 100.0 % < 100.0 µm | details |
| Graphite | <20µm | app. 6µm | details |
| graphite | < 1cm | < 45µm | details |
| graphite | 2 mm | < 80 µm | details |
| Graphite (3 samples) | < 3 mm | < 45 µm | details |
| Gras (wet) | ca 5 cm | 5-6 mm | details |
| gray cast iron | Ø 5 cm | < 10 mm | details |
| Green alge (Haematococcus Pluvialis) | <150µm | d50 < 15µm | details |
| gypsum | 5 mm | < 0.1 mm | details |
| Gypsum | < 2 cm | < 0,5 mm | details |
| Gypsum (1) / Dolomite (2) | 1 cm | 58%<0,2mm | details |
| Gypsum Cardboard | 11 cm | 75.0 % < 40.0 µm | details |
| Gypsum rock sample | 20.0 mm | 100.0 % < 250.0 µm | details |
| Hair | 40 mm | 90 % < 100 µm | details |
| hair | < 1cm | ~ 500µm | details |
| hair | 3-4 cm | < 500µm | details |
| Hair (human) | <3-5mm*1 | <300µm | details |
| Hamp seeds | < 4mm | < 750µm | details |
| Hard Coal | < 10 mm | < 200 µm | details |
| hard-PVC | 1 cm | <1 mm | details |
| hay | 10 - 20 cm | < 0,25 mm | details |
| heazlewoodite | 1-2mm* | ca. 80% <5 | details |
| hemp (stalk) | < 1 cm (diameter) | < 0,25 mm | details |
| hemp fibers | 10.0 mm | 50.0 % < 500.0 µm | details |
| High Density Polyethylene (HDPE) | < 4 mm | < 0,4 mm | details |
| Hippophae rhamnoides - dry parts and seeds of plant | < 2 cm | < 0,5 mm | details |
| Horn (keratin - goat) | 4 cm | < 120 µm | details |
| Hydroxylapatite | <25µm | d50 < 500 nm | details |
| Hydroxylapatite | 2 cm | 1,4mm - 8 mm | details |
| Icing Sugar | 300µm | d90 < 10µm | details |
| Indigo (Dye) | < 50 µm | d50 < 250 nm (d50 < 150 nm reached) | details |
| Ion exchange resins | ~ 500 µm | d50 < 5 µm | details |
| Iron (pellets) | < 1cm | 100% < 75 µm; d50 < 30µm | details |
| Iron ore | < 4cm | < 100µm | details |
| iron ore | 5 mm | < 140 µm | details |
| IRON ORE PELLETS | 20.0 mm | 95.0 % < 3.0 mm | details |
| Iron powder (press cake) | < 60 mm | < 200 µm | details |
| Iron silicide strips | 8 cm | < 0,25 mm | details |
| iron slag | < 5 cm | < 15 mm | details |
| Isolation wool | 10.0 mm | 50.0 % < 15.0 µm | details |
| juniper berries (dried) | < 14mm | < 1mm | details |
| Kaffee | | | details |
| Kalahari melon seeds | 10 mm | < 2 mm | details |
| Kalknatronglas, Borosilikatglas | < 3 mm | d50 < 100 nm | details |
| kibbled Soy | < 2 mm | < 500 µm | details |
| Lactose | < 400 µm | d50 < 20 µm | details |
| Lead Oxide (1-2) / Bismuth Titanate (3-4) | <74µm | d50 < 1,5µm | details |
| Leaded glass powders | <40µm | d50 < 1µm | details |
| leather | < 30 cm | 0,5-10 mm | details |
| leather bracelet (black) | 20 cm | < 2 mm | details |
| Leather sample | 80 mm | 90.0 % < 1 mm | details |
| Leaves (2 samples) | 3 – 4 cm | < 0,25 mm | details |
| Leek | 30 cm | 99 % < 0,5 mm | details |
| Leucit | 4 mm | < 100 nm (d50 reached) | details |
Li-Managanese Phosphate (trials 1-2)
Li-Cobalt Phosphate (trials 3-4) | 10µm | d50 < 60nm | details |
| lime | < 8 mm | < 200 µm | details |
| limestone | < 1 mm | 90 % < 63 µm | details |
| Limestone | < 1 cm | d50 < 1 µm | details |
| Limestone | < 4 mm | < 63 µm | details |
| Limestone | ~ 0,5 mm thickness | < 20 µm | details |
| Limestone | 10mm | 65%<1µm | details |
| limestone (Kalkstein) | ca. 200µm | < 3µm | details |
| limestone (Kalkstein) | <~8mm | <150µm | details |
| Liquorice Root Fragments | 150.0 mm | 100.0 % < 2.0 mm | details |
| Lithium cobalt oxide | 70µm | 100% < 4µm | details |
| magnesium carbonate | < 2mm | < 200 µm | details |
| Magnesium diboride | d50 < 10,6µm | d50 < 1µm | details |
| magnesium oxide (sintered - MgO) | 2,5 cm | < 63µm | details |
| Maize root (fresh) | < 2cm | < 1mm | details |
| Manganese Alloy | < 6 cm | < 150 µm | details |
| Manganese dioxide (300g < 30µm = 1; 15g <0,5µm =2/3) | 120µm | d50 < 3,1µm / d90< 17,2µm | details |
| Manganese Ore | 355.0 µm | 355.0 % < 300.0 µm | details |
| Manganese-Flakes | 10 mm | < 200 µm | details |
| marble | < 8mm | < 50µm | details |
| metal turning chips | 40x2x0,1 mm | < 800µm | details |
| meteorite samples | 3 mm | 50 % < 200.0 µm | details |
| mica (nealed) | 150 µm | 22 % < 20 µm | details |
| Mineral | < 60µm | d50 < 300nm | details |
| mineral wool | 4 cm | < 1 mm | details |
| mineral/soil | up to 10cm roots | homogenous | details |
| Mineral: Perovskite | powder | d50<0,29µm d90<0,49µm | details |
| Minerals | < 7 mm | d90 < 5 µm | details |
| Minerals and Slag | 50.0 mm | 95 % < 0.5 mm | details |
| Mistletoe beeries | 1 cm | < 2 mm | details |
| Mix of Fungi (Edible Mushrooms - dried) | 50 mm | 95 % < 2 mm | details |
| Montmorillonite | < ca. 130µm | d50 < 1,5µm | details |
| muck (from chicken farm, dried) | 70mm | < 0,5mm | details |
| Musli bars | < 12 cm | < 2 mm | details |
| Na-Montmorillonite | <30µm | d50<0,5µm | details |
| natural amorphous silica | < 100 µm | < 10 µm | details |
| Nickel (pure powder) | ~ 500µm | d90 < 160µm | details |
| NiMH batteries | < 8 cm | < 100 µm | details |
| noodles | < 2-3cm | < 0,25mm | details |
| Oil palm Empty fruit bunch | < 3 cm | < 0,2 mm | details |
| Oil Palm empty Fruit Bunch Fiber | 5x1 mm | d50 < 40µm | details |
| Olives (pickled) | 20mm | homogeneous | details |
| orangecalcite | 6 cm | < 8 mm | details |
| Ore | < 6cm | < 150µm | details |
| Ore sample | < 8mm | < 1,12 mm | details |
| organic fibers (dry sample) | < 5 cm | < 1 mm (lenght) | details |
| palm shells | < 3 cm | < 0,5 mm | details |
| paper sheets (for printers) | 29,8 cm x 20,9 cm | < 500 µm | details |
| paprika (dried - sweet pepper) | 10 x 2 cm | 99% < 1mm | details |
| Parts of olive trees and citrus fruits dried | max 2 cm | < 200 µm | details |
| PC Board | < 20x14cm (before pre cutting) | < 1mm | details |
| PE-black | < 5 mm | 315-1000 µm | details |
| Peanuts | <20mm | ~500µm | details |
| peat | < 3 cm | < 250 µm | details |
| pebbles | 5 cm | < 10 mm | details |
| Pepper (green chilies - dried) | 2 cm | < 0,5 mm | details |
| Peppercorns (Black) | < 5mm | < 1,5 mm | details |
| Perlite (Obsidian) | ~ 3mm | d90 < 20µm | details |
| PET (several kind of pre forms & lids) | < 15 cm | < 0,5 mm | details |
| PET Flakes | 10 mm | 80.0 µm - 160 µm | details |
| PET Flakes | < 2 cm (long) | 0,5-1,0 mm | details |
| PET Preform | ca 10 cm | < 0,25 mm | details |
| PET preform | 15 cm long | < 1 mm | details |
| PET preforms | 10 cm | < 4 mm | details |
| PET-tubes | 130x25mm | <1mm | details |
| PETG | 5mm | 1mm | details |
| Petroleum coke | 5 mm | < 180 µm | details |
| Pharmaceuticals pills | 2.0 cm | 90.0 % < 120.0 µm | details |
| pigment in suspension (yellow) | < 5 µm | d50 < 0,7 µm | details |
| pine needles | 1 – 2 cm | fine powder | details |
| Pineapple | 25 cm | 100 % < 1 mm | details |
| pistachios nuts (kernels) | 2cm | pasty mass | details |
| plastic - PP EPDM, PS, PP, PA | ca 10 mm | < 2 mm | details |
| Plastic pellets (different kinds of pastic waste) | < 5 mm (diameter) | < 250 µm | details |
| plastics (mixture) | < 4 cm | < 1 mm | details |
| plastics and rubber | 4.5 x 2.5 | < 2,00mm | details |
| Plums (fresh with stone) | 50 mm | 5 mm | details |
| PMMA - (C5O2H8)n | 70.0 mm | 100.0 % < 5.0 mm | details |
| PMMA pellets (Polymethylmethacrylat) | 3 mm | < 0,2 mm | details |
| PMMA-Sample | 1.0 cm | 95 % < 2.0 mm | details |
| Polishing suspension Cerium dioxide | < 40µm | 95% < 1µm | details |
| polyamid N6 | 3mm | app. 500µm *1 | details |
| Polycaprolacton (PCL) | 3-4 mm | < 200 µm | details |
| polycarbonate | 5 min | < 0,5 mm | details |
| Polycarbonate (PC) | 1.0 cm | 50.0 % < 300.0 µm | details |
| Polyester (18-18) | 1.0 cm | 99.0 % < 1.0 mm | details |
| Polyester (Hard PE) | < 7 mm | < 0,2 mm | details |
| Polyethylene | 300.0 µm | 100.0 % < 100.0 µm | details |
| Polyethylene (PE) | < 5 mm | < 0,25 mm | details |
| Polyethylene Powder | 300.0 µm | 100.0 % < 100.0 µm | details |
| Polymer | < 4 mm | < 0,5 mm | details |
| polymer resin | 3 cm | 95 % < 500µm | details |
| polymeric concrete | < 95 mm | < 2 mm | details |
| Polymeric Sulfur sample | 90.0 mm | 50.0 % < 35.0 µm | details |
| Polypropylene Granulates | 4 mm | 90 % < 500 µm | details |
| polysaccaride (freeze dried) | < 5mm | < 20µm | details |
| Polyvinyl Butyral (PVB) | 20 cm | 80.0 % < 350.0 µm | details |
| pomace of pears | 2-3cm | < 0,25 mm | details |
| Popcorn | 25 mm | 90 % < 2 mm | details |
| Porcelaine | < 10 mm | d50 < 0,5 µm (d50 < 1 µm reached) | details |
| potassium chloride (KCl) | 2cm | < 500µm | details |
| press mud Almerich | app. 1cm | 50%<18,1µm 90%<87.3µm | details |
| Pressed and Dried Food Pellet | 20.0 mm | 100.0 % < 250.0 µm | details |
| printed circuit board (PCB) | < 1 cm (long) | < 100 µm (metal content will become flakes) | details |
| pumpkin | 12 mm | 150 µm | details |
| PVC | | | details |
| PVC (blue) | 5 mm | < 2mm | details |
| PVC Woodcomposites (4 Samples) | | | details |
| PVC-free Floor Covering (PVB) | 20 cm | 80.0 % < 350.0 µm | details |
| Pyrite | 1.0 mm | 75.0 % < 50.0 µm | details |
| Quick lime sample (gray and beige) | < 2 cm | < 0,1 mm | details |
| Raisins | ~ 12 mm | 100 % < 1 mm | details |
| raw clay | < 3,5 cm | < 0,5 mm | details |
| Rawhide Dog Bones | 12cm | < 2mm | details |
| Resign for powder coating | < 1 mm | 100 % < 200 µm | details |
| resin | 3 - 4 cm | < 1 mm | details |
| Rhenium | < 5 mm | < ~0,3 mm | details |
| Rice | < 5 mm | < 200 µm | details |
| Rice (jap.) | whole grains | <1mm or finer | details |
| roots (dry; no soil rests) | 2.0 mm | < 80.0 µm | details |
| Roots With Soil (dried) | 15-20 mm | 95 % < 1.0 mm | details |
| rose quartz / aquamarine | <8-10mm | d90 < 15µm | details |
| Rubber Powder | 500.0 µm | 90.0 % < 200.0 µm | details |
| Ruby and YAG sample | 5.0 mm | 100.0 % < 70.0 µm | details |
| rye | 10 mm | < 300 µm | details |
| Salt | <50mm | < 45µm | details |
| salt | 4mm | 74% <315µm | details |
| salt with iodine | ~ 1mm | <100µm | details |
| sand | <1mm | < 63µm | details |
| sandstone | 25mm | <250µm | details |
| Scandia Stabilized Zirconia | 10.0 mm | 50.0<50.0 µm | details |
| sea shell | <10mm | d50 <0,3µm | details |
| Secondary Fuels | 40.0 mm | 100 % < 4.0 mm | details |
| Secondary Fuels | 50.0 mm | 100.0 % < 250.0 µm | details |
| Shark fins | 6 cm | < 4 mm | details |
| Shark Teeth | 15 mm | 100.0 % < 1000.0 µm | details |
| Shredded electronic scrap | < 5 cm (long) | 0,1 mm (not reachable) | details |
| Si, C and SiC | <50µm *1 | aerosis /high pressure !!*2 | details |
| SiC (1= SiC 0-25mm, 2= Sika Ref I) | max. 25mm | 89% <180µm | details |
| Silacron (Quarz acrylic compound) | < 6 cm | 10 mm | details |
| Silica | < 30 µm | d50 < 360 nm; (d50 < 100nm desired) | details |
| Silica gel (desiccant beats) | 2-5 mm | d50 < 25 µm | details |
| silica sand | 100µm | ca. 90% < 10µm | details |
| Silicate glas | < 125µm | d50 <5,1µm | details |
| silicium | < 10mm | d50<1,4µm d90<5,5µm | details |
| Silicium oxide (molten) | 6 cm | 6 mm | details |
| silicon | 3cm* | 0,2%>315µm 52,5%>63µm | details |
| Silicon (metal) | < 4 mm | 90 % < 160µm | details |
| Silicon Carbide | 40µm | d50 <0,4µm | details |
| Silicon carbide | <10mm | < 1mm | details |
| Silicon powder | < 50 µm | d50 < 460nm | details |
| sintered alloy of Ti-Fe-Ni | < 10 mm | < 100 µm (10 % <100µm reachable) | details |
| sintered tungsten carbide | < 2 cm (sintered) | < 100 µm | details |
| sisal | 20 cm | < 2 mm | details |
| slag | < 7cm | < 63µm | details |
| slag | < 5 cm | < 1 mm | details |
| Slag | < 12mm | < 150µm | details |
| Slag | ~ 90µm | < 30µm | details |
| Slag with elemental copper content | 3 cm | < 3 mm | details |
| sludge | 30 mm | < 0,2 mm | details |
| sodium silicate (water glass) | 6 cm | < 10 mm | details |
| sodium waterglass (sodium silicate) | 1 mm | < 50 µm | details |
| soft plastics | < 1cm | < 500 µm | details |
| Soil | < 8 mm | < 125 µm | details |
| Soil | <4,5cm | | details |
| soil | < 10 mm | 90% < 90µm | details |
| Soil | 3cm* | <2mm: | details |
| soil (without stones) | < 2cm | homogen, fine powder | details |
| Soil sample | 6 cm | fraction >2mm | details |
| Soil sample | 5 cm | <2mm after: 3. application 94% | details |
| Soil sample (B-10-37 4,9~5,0) | <3cm | 83,4% < 2mm | details |
| soil sample (deagglomeration) | 15.0 mm | 50.0 % < 2.0 mm | details |
| Solid alternative fuel | | < 1 mm | details |
| soy | app. 2cm | paste | details |
| Spirulina, dried powder | ~ 100 µm | d50 < 1 µm ( < 730 nm has been reached) | details |
| spruce needles | 15mm | < 100µm | details |
| Stainless steel (powder) | 70 µm | flat flakes (up to 300µm) | details |
| Steel granulate | < 7mm | < 1mm | details |
| Steel making Slag Converter and Iron Sinter | 0.25 mm | 80.0 % < 1 µm | details |
| Steel Slag | 300 µm | < 1 µm | details |
| Stinging nettle (dry stem material) | 20 cm | < 2 mm | details |
| stone | 3-5 mm | 500 µm | details |
| stone | ~ 8 mm | d90 < 30 µm | details |
| stone sample TR | < 2 cm | 71-630 µm (82% reachable) | details |
| stone samples | < 6 cm | 71-630 µm | details |
| Stone Wool | 3.0 cm | 90.0 % < 100.0 µm | details |
| stones | 0.3 cm | < 100µm | details |
| stones (sample: No. 3) | 2 mm | d90 < 63µm | details |
| stones with quartz | < 10 cm | d50 < 50 µm | details |
| Straw (Cereals waste particles) | ~ 1 cm | < 0,25 mm | details |
| Straw sample | 10 - 20 cm | 90 % < 0.25 mm | details |
| Strontium Nitrate | < 10 mm | 90.0 % < 200.0 µm | details |
| sugar beet pulp | app. 2-3 mm | app. 50-100 µm | details |
| Sugar extrafine | < 2 mm (largest particle) | 250 -500 µm (fraction) | details |
| Sunflower Seeds | < 12 mm length | < 1 mm | details |
| sunflower seeds | < 1cm | < 0,5mm | details |
| sweet grass (Miscanthus) | < 3 cm | up to 300 µm | details |
| Tablets | 10 mm | d50 < 50 µm | details |
| tablets of Vitamin C (1, red) and valerian (2, brown) | 10mm | <200µm | details |
| TANTALUM | 10.0 cm | 1.0 % < 1.0 mm | details |
| Tea | 3.0 mm | 99 % < 500.0 µm | details |
| Tea (leaves, dried) | 8 mm | 1 mm | details |
| textile | 45.0 cm | 100.0 % < 15.0 cm | details |
| Thermoplastic Starch | 3.0 mm | < 0.2 mm | details |
| thermosetting resin | 20 mm (flakes) | < 120 µm (d50 < 40 µm) | details |
| Tire Pieces | 7cm | < 0,25mm | details |
| TiSi2 | powder | d50 <0,5µm | details |
| TiSi2, Titansilicid | powder | | details |
| titandioxid | nanopowder | 90%<10-100nm | details |
| Titanium Boride Powder (10 micron) | ca 10µm | < 2µm | details |
| Titanium dioxide | 10.0 mm | 100.0 % < 1.0 µm | details |
| Titanium dioxide | | | details |
| Titanium dioxide (TiO2) | 100.0 µm | 100.0 % < 30.0 µm | details |
| Titanium dioxide paste | <30µm | d50 < 0,5µm | details |
| titanium turnings | < 3 cm | d50 < 10 µm | details |
| Titansilicid | << 1mm | << 1mm | details |
| Tomato seeds | app. 3mm | homogenous suspension | details |
| tooth | 3 mm | d50 < 150 µm | details |
| Tuff (1-2) and Microsilica (3-4) | < 100µm | <0,320µm | details |
| Tumeric powder | 150.0 µm | < 40.0 µm | details |
| tungsten powder grained, agglomerated | ca. 70 µm | d50 < 5 µm (d50 < 7 µm reached) | details |
| tungsten(VI)oxide WO3 | d90 < 25 µm | d50 < 0,5 µm
d95 < 1,0 µm | details |
| Tungsten-Rhenium | 4 mm | 63-160 µm | details |
| turquoise (China) | 3 – 4cm | < 1 cm | details |
| Two rock samples | 90.0 mm | 100.0 % < 500.0 µm | details |
| tyre | 5 x 2cm | < 2mm | details |
| Valerian tablet (coated) | 10 mm | 100 % < 1 mm | details |
| Vanadyl Pyrophosphate | 2mm | < 80µm | details |
| Varistor Green Body | 500 g | < 0,5 mm | details |
| Vine leaves (Vitis vinifera) | < 30 mm | < 0,2 mm | details |
| Vine stem (Lot 5.3) | <5mm | powder | details |
| Vulcanized Rubber | 50 mm | 90 % < 200 µm | details |
| waste (rests of car scrap yard) | 15 cm | <2 mm | details |
| waste of leaves and branches | 3-8 cm | < 0,25 mm | details |
| Wheat (Triticum) | < 6 mm | < 0,5 mm | details |
| Wheat straw | < 20 cm | < 63 µm | details |
| Wood | < 14 cm | < 1 mm / < 4 mm | details |
| wood | < 7cm | <250µm | details |
| wood | app. 1 x 0,4cm*3 | homogenous, lightly like fibres | details |
| Wood | < 10 mm | < 1 mm | details |
| wood (biomass) | < 13cm | < 4mm | details |
| Wood (dried; natural and previously treated) | < 3 cm | < 500 µm | details |
| Wood (wet) | 2 cm | 1 mm (thick) | details |
| wood and bark | 6 cm | < 1 mm | details |
| wood chips (dry) | < 3 cm | < 2 mm | details |
| wood shavings | 3 mm | < 0,25 mm | details |
| wooden chips (soft) | 6.0 cm | 90.0 % < 4.0 mm | details |
| Wool | 20 cm | < 0.2 mm | details |
| Wool Fibers | very long | d50 < 20µm (d50 < 28 µm reached) | details |
| Yttrium phosphate | ca. 50µm | d50 < 5 µm | details |
| Yttriumoxide | app. 30µm | app. 100µm | details |
| Zeolite | | d50 ~ 0,5µm | details |
| Zinc oxide | <15µm; d50<1µm | 50%<0,6µm; 90%<2,3µm | details |
| Zircon (two samples) | ~ 60 µm | d50 < 300 nm (rached with PULVERISETTE 7 p.l.) | details |
| Zirconium (raw material) | < 12 mm | < 100 µm | details |
| Zirconium dioxide | app. 5cm (long) | < 8mm | details |
| Zirconium dioxide + yttrium trioxide | 65 mm | 0,1 - 0,5 mm | details |
| zirconium hydroxide | 5 mm | 87% < 180 µm | details |
| Zirconium oxide | < 100 µm | d50 < 200 nm (d50 < 63 nm reached) | details |
| Zirconium oxide | 3 cm | 100-300 µm | details |